Database of Zeolite Structures
 
Framework Type SFS
Powder Diffraction Pattern for SSZ-56
Input Parameters
  Wavelength:  or
  2θ range:
  Step size:
  Polarization factor:
  Background:
  Reference peak is
    peak closest to °2θ
    reflection (hkl)
       scaled to
  Intensity axis:
     
Peak shape
  Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
  FWHM = sqrt (U + V tan θ + W tan2θ)
  Mixing parameter (n): %
  Peak range: FWHM
  Peak width:
    set UVW at: U =   V =   W =
    FWHM =
    FWHM =
  FWHM =
   
Select Output
 
List hkl and intensity
List powder pattern
plot powder pattern
Crystal Data
  Space Group: P 1 21/m 1   (# 11)   
  Cell parameters: a = 13.9483 Å b = 19.8958Å c = 12.3613 Å
    α = 90° β = 106.676° γ = 90 °
  Chemical Formula |(H2O)10.0 | [Si54.7B1.3O112]-SFS
  Refinement:
  Comment: unique axis b
  Reference: Elomari, S., Burton, A., Medrud, R. C. and Grosse-Kunstleve, R.
Microporous Mesoporous Mat., 118, 325-333 (2009)
  Atomic Coordinates:          
   
Atom
Form Factor
x
y
z
PP
B(iso)
   
  Si1
Si
0.4158 0.1753 0.6388 1 0.08
  Si2
Si
0.2878 0.1262 0.3975 1 0.08
  Si3
Si
0.2768 0.1278 0.7862 1 0.08
  Si4
Si
0.4155 0.5638 0.643 1 0.08
  Si5
Si
0.428 0.171 0.2637 1 0.08
  Si6
Si
0.4332 0.5573 0.2679 1 0.08
  Si7
Si
0.4274 0.1725 0.0095 1 0.08
  Si8
Si
0.0716 0.1745 0.6427 1 0.08
  Si9
Si
0.0799 0.1742 0.3912 1 0.08
  Si10
Si
0.276 0.5309 0.7939 1 0.08
  Si11
Si
0.289 0.5338 0.3992 1 0.08
  Si12
Si
0.427 0.5585 0.0153 1 0.08
  Si13
Si
0.0697 0.5589 0.6589 1 0.08
  Si14
Si
0.078 0.5586 0.4011 1 0.08
  O1
O
0.5131 0.1273 0.683 1 0.24
  O2
O
0.357 0.1582 0.5098 1 0.24
  O3
O
0.453 0.25 0.656 1 0.24
  O4
O
0.339 0.1575 0.709 1 0.24
  O5
O
0.1781 0.154 0.356 1 0.24
  O6
O
0.2862 0.046 0.41 1 0.24
  O7
O
0.3329 0.144 0.296 1 0.24
  O8
O
0.1658 0.1548 0.7481 1 0.24
  O9
O
0.3241 0.1513 0.9156 1 0.24
  O10
O
0.278 0.0486 0.782 1 0.24
  O11
O
0.4766 0.6319 0.665 1 0.24
  O12
O
0.3442 0.5587 0.721 1 0.24
  O13
O
0.495 0.504 0.674 1 0.24
  O14
O
0.3561 0.5629 0.5132 1 0.24
  O15
O
0.44 0.25 0.292 1 0.24
  O16
O
0.409 0.1582 0.131 1 0.24
  O17
O
0.3301 0.5537 0.2977 1 0.24
  O18
O
0.4093 0.5504 0.1359 1 0.24
  O19
O
0.451 0.25 0.994 1 0.24
  O20
O
0.5192 0.1278 0.998 1 0.24
  O21
O
0.1064 0.1662 0.5279 1 0.24
  O22
O
0.9771 0.128 0.639 1 0.24
  O23
O
0.042 0.25 0.654 1 0.24
  O24
O
0.05 0.25 0.353 1 0.24
  O25
O
0.9861 0.1271 0.334 1 0.24
  O26
O
0.1662 0.5566 0.7581 1 0.24
  O27
O
0.3212 0.5512 0.9235 1 0.24
  O28
O
0.1768 0.5602 0.366 1 0.24
  O29
O
0.5 0.5 0 1 0.24
  O30
O
0.996 0.498 0.667 1 0.24
  O31
O
0.0926 0.5511 0.5368 1 0.24
  Ow1
O
0.766 0.25 0.198 1 14.8
  Ow2
O
0.856 0.183 0.876 1 14.8
  Ow3
O
0.073 0.122 0.007 1 14.8